Kitovi

ALUMINIUM PUTTY: 0RS009-0.5KG, 0RS009-1.8KG, 0RS009-1KG

 

Characteristics:

Fine-grained filling putty with aluminum flakes. It is characterized by particular ease of modeling in thin layers and ease of processing with high grit abrasives starting from P150. The putty has high resistance to elevated temperatures and mechanical loads. The ability to use high grit abrasives (coarse sanding P150) and the adjusted hardness of the putty to paint coatings eliminates the formation of transitions between the putty and the repaired surface. For filling irregularities on steel surfaces exposed to elevated temperatures and mechanical loads (e.g., vibrations). Intended for manual and machine processing with dry abrasives. It is easy to model, very soft in grinding processing. Does not clog abrasive material during sanding. It has very good adhesion to the substrate, used among other things to reinforce the surface weakened after sheet metal repair, increasing the mechanical strength of the repaired element.
Does not require the use of finishing putty.

Usage:

The repaired substrate must be clean, dry, degreased, and matted. Thoroughly mix the putty mass with the hardener in an amount of 2-3% by weight, then apply to the substrate for about 5 minutes at 20 ^oC - higher temperature shortens the product's life and accelerates the curing process.

NOTE: Overdosing the hardener may cause discoloration of the topcoat. It is not recommended to use the product at temperatures below 15 ^oC.